Bone grafts and methods of making and using bone grafts

ABSTRACT

Provided herein are bone grafts and methods of making and using the same, as well as products and kits that include such bone grafts. In particular, bone grafts are provided that include collagen Type I and one or more different types of mineral compositions having different dissolution properties and/or sizes, to enhance bone regeneration throughout the bone healing phase.

CROSS REFERENCE TO RELATED APPLICATION

This is a divisional application of U.S. patent application Ser. No. 14/177,967, filed Feb. 11, 2014, which is incorporated by reference herein in its entirety for all purposes.

FIELD OF THE INVENTION

The present invention generally relates to bone grafts, and methods of making and using the same. The invention also relates to bone grafts that include collagen Type I and one or more different types of minerals having different dissolution properties, and/or one or more sizes. Further included are kits and implants having the present bone grafts; and methods of making and using the present bone grafts.

BACKGROUND

Bone generally has the ability to regenerate completely, e.g., after a fracture but requires a very small fracture space or some sort of scaffold to do so. Bone grafting is a surgical procedure that replaces missing bone to repair bone fractures that are very complex, fail to heal properly, or pose a significant health risk to the patient.

Bone grafts may be autologous (bone harvested from the patient's own body, often from the iliac crest), allograft (cadaveric bone usually obtained from a bone bank), or synthetic (often made of hydroxyapatite or other naturally occurring and biocompatible substances) with similar mechanical properties to bone. Most bone grafts are expected to be reabsorbed and replaced as the natural bone heals over a few months' time.

Bone grafts are osteogenic if they contain viable cells that are capable of bone regeneration. The current gold standard in bone graft substitutes for spine and long bone applications is autograft (i.e., using the patient's own tissue), followed by allografts. Autografts are considered osteogenic, as they contain a high number of bone forming cells. However, autographs may have limited availability and they are limited by donor site morbidity. Also, autografts may require multiple surgeries. Allografts are limited by the large variability in performance due to source and processing steps.

There is a need to produce superior bone grafts that are osteogenic and/or are able to enhance bone regeneration throughout the bone healing phase.

SUMMARY

According to non-limiting example embodiments, the present invention provides bone grafts that include collagen and one or more minerals having different dissolution properties or rates and/or sizes, to enhance bone regeneration throughout the bone healing phase. These minerals can be, for example, in the form of a calcium phosphate, carbonate apatite, and/or calcium carbonate.

Other example embodiments are directed to methods for preparing the bone grafts provided herein. Further example embodiments are directed to methods that include administering a bone graft substitute to a mammal by surgically inserting one or more of the present bone grafts into a mammal. The bone grafts may be administered for example by themselves e.g., in the form of a strip, putty, gel and sponge, or the bone graft may be available in conjunction with an implant, such as being incorporated therein or thereon.

Yet further example embodiments are directed to implants or other devices that include one more of the bone grafts provided herein therein or thereon. Other example embodiments are directed to kits that include one or more of the present bone grafts and/or components or ingredients that may be combined mixed or treated to prepare the present bone grafts, as well as instructions, devices, implants, tools or other components that may assist with making or using the present bone grafts.

BRIEF DESCRIPTION OF DRAWINGS

Non-limiting example embodiments are described herein, with reference to the following accompanying Figure:

FIG. 1 is a flow chart of an example method of preparing a bone graft according to non-limiting examples of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is drawn to bone grafts and methods for making and using such bone grafts, as well as kits and implants or other devices including the same.

While the example embodiments are described to be used in conjunction with healing bone fractures, it should be understood that these bone grafts may be used for other purposes and therefore the present invention is not limited to such applications. In view of the teachings provided herein, one having ordinary skill in the art would recognize other applications for which the bone grafts of the present invention could be used, and would be able to use the bone grafts and methods of the present invention in other applications. Accordingly, these alternative uses are intended to be part of the present invention.

Additional aspects, advantages and/or other features of example embodiments of the invention will become apparent in view of the following detailed description, taken in conjunction with the accompanying drawings. It should be apparent to those skilled in the art that the described embodiments provided herein are merely exemplary and illustrative and not limiting. Numerous embodiments of modifications thereof are contemplated as falling within the scope of this disclosure and equivalents thereto.

In describing example embodiments, specific terminology is employed for the sake of clarity. However, the embodiments are not intended to be limited to this specific terminology. Unless otherwise noted, technical terms are used according to conventional usage.

As used herein, “a” or “an” may mean one or more. As used herein “another” may mean at least a second or more. Furthermore, unless otherwise required by context, singular terms include pluralities and plural terms include the singular.

As used herein, the term “mammal” is intended to include any “subject” or “patient” animal, (including, but not limited to humans) to whom the present bone grafts may be administered. A subject or patient or mammal may or may not be under current medical care, and may or may not have had one or more prior treatments. As would be apparent to those skilled in the art, the formulations may be different for non-humans than for humans.

As used herein, “an effective amount” refers to an amount of the specified constituent in a composition or formulation, or an amount of the overall formulation that is effective in attaining results, the purpose for which the constituent or composition is provided. Therefore, an effective amount of a bone graft formulation would be an amount suitable for achieving the desired bone graft effect in a subject, such as a mammal (e.g., human) to which the present bone graft is administered.

Numerical data may be presented herein in a range format. It is to be understood that such range format is used merely for convenience and brevity and should be interpreted flexibly to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited.

According to non-limiting example embodiments, bone grafts may be prepared that include collagen and one or more minerals, including but not limited to calcium phosphates, carbonate apatite, and/or calcium carbonate having both “fast” and “slow” dissolution rates. The “fast” or “faster” dissolution rates help bone healing in the early phases (from e.g., weeks up to a couple of months after the bone graft has been implanted into a patient), while the minerals having slower dissolution rates can be present for e.g., up to two years in the patient after implantation. The terms fast and slow are relative terms, but are meant to be relative with respect to each other, and the relative rates would be apparent to those skilled in the art in the context of the present disclosure in the bone grafting context. That is, a skilled practitioner would be able to determine which minerals may have faster or slower dissolution rates that may be appropriate in the bone grafting context for dissolution at a desired rate.

Therefore, a goal of the present invention is to produce a bone graft that circumvents limitations of prior bone grafts by: (1) regenerating bone without the need to harvest bone from the patient; (2) having a bone regenerating material with lower variability in osteogenic properties relative to allograft; and (3) including mineral (e.g., calcium phosphate, carbonate apatite, and/or calcium carbonate), with or without the optional ingredients of demineralized bone matrix (DBM), and with or without hyaluronic acid. The incorporation of more than one mineral will provide a range of dissolution rates, which will allow for the bone graft to enhance bone healing in both early and late phases of bone healing.

These embodiments of the present bone grafts will thus, be an alternative to the use of autografts and allografts. These embodiments will also be an alternative to currently available collagen-based bone grafts because they will have minerals incorporated, which will have one or more dissolution rates to enhance bone healing in both early and late stages.

Minerals differing in dissolution rate and/or size can be used in the present bone grafts. The possible combinations of minerals in these embodiments will interact with new bone formation throughout the bone healing process. For instance, if two or more minerals are chosen, then one mineral will be active in the early bone healing, and the second mineral will be active in the later stage of bone healing. According to alternative embodiments, a third or more mineral having yet a different dissolution rate and/or size can be incorporated.

An additional benefit of the present bone grafts in relation to the different sizes and/or dissolution rates of the minerals, is that the mineral with the “slow” dissolution rate may also have a porous structure. This porous structure will help in the entrapment of growth factors and/or osteoprogenitor cells, which literature has suggested as being the mechanism for osteoinduction in calcium phosphate-based materials.

Thus, according to non-limiting example embodiments, the present invention provides bone grafts that include collagen type I and at least one, two, or more different types of minerals, such as calcium phosphates, carbonate apatites, and/or calcium carbonates, having different dissolution properties/rates and/or different sizes than one another, to enhance bone regeneration throughout the bone healing phase.

According to non-limiting example embodiments, bone grafts are provided which include: 20% to 95% by weight (with respect to the final product) of Collagen Type I and 20% to 95% by weight (with respect to the final product) of minerals having different dissolution properties and/or sizes than one another. According to example embodiments, the minerals may include one or more minerals selected from calcium phosphates, carbonate apatites, and/or calcium carbonates,

According to example embodiments, the collagen Type I may be from bovine or porcine source and may be obtained from either skin (dermal) or tendon.

Bone grafts according to these embodiments may further include at least one further ingredient selected from: 0.2 to 20% by weight hyaluronic acid with respect to the total weight of the bone graft, acid (such as hydrochloric acid) or base (such as sodium hydroxide) in an amount necessary to adjust the pH, which amount may be for example 0.1 to 20% by weight with respect to the total weight of the bone graft, and 20% to 95% by weight DBM.

Further provided herein are methods of making the present bone grafts that include mixing 20% to 95% by weight Collagen Type I with one or more minerals having at least two different dissolution rates or sizes; refrigerating the mixture for 30 minutes to 5 hours; neutralizing the mixture until the pH is between 6.5 and 8.5; refrigerating the mixture for 1 hour to 24 hours; blast chilling the mixture in a freezer at e.g., −40° C., or at least a temperature of less than −20 ° C., for 1 hour up to 24 hours; freeze drying the mixture for 24 to 72 hours to form a mixture; physically or chemically cross-linking the mixture; and freeze drying the mixture. The method may further include stamping or cutting out the mixture to desired dimensions.

According to non-limiting example embodiments, provided herein are methods of making the present bone grafts that include mixing 20% to 95% by weight Collagen Type I with 0.2 to 20% by weight hyaluronic acid until a desired consistency is reached and obtaining a desired pH of the mixture; refrigerating the mixture for 20 to 72 hours; further mixing to form a homogenous collagen mixture; weighing out at least one of mineral and demineralized bone matrix (an optional extra ingredient); mixing the mineral and optionally DBM with the collagen mixture; refrigerating the mixture for 30 minutes to 5 hours; neutralizing the mixture (e.g., with HCl or NaOH) until the pH is between 6.5 and 8.5; pouring the mixture into a tray; refrigerating the mixture for 1 hour to 24 hours; blast chilling the mixture in a freezer at a temperature of less than or equal to −20° C. for 1 hour up to 24 hours; freeze drying the mixture for 24 to 72 hours to form a mixture; physically or chemically cross-linking the mixture; freeze drying the mixture; and stamping or cutting out the mixture to desired dimensions.

The mineral of these embodiments may include for example, one or more of the following: beta-tricalcium phosphate (size ranging from 75 nm to 500 μm), carbonate apatite (size ranging from 75 nm to 500 μm), and calcium carbonate (size ranging from 75 nm to 500 μm). Thus, example embodiments include collagen Type I and one or more different types of minerals, and/or one or more sizes.

According to example embodiments, the total weight percent of mineral in the bone graft is from 20% to 95% by weight with respect to the total weight of the bone graft.

According to non-limiting example embodiments, the total weight percent of DBM in the bone graft may be from 20% to 95% by weight with respect to the total weight of the bone graft.

Non-limiting example methods according to the present invention are depicted for example, in the flow chart of FIG. 1. As shown in FIG. 1, in example embodiments, collagen is first mixed with HCl. As indicated above, these ingredients may be mixed until a desired consistency is reached. Although not specifically set forth in the flow chart of FIG. 1, a desired pH of the mixture may then be reached. The mixture may then be refrigerated and allowed to swell for up to 20 hours. According to these embodiments, an optional ingredient of DBM is added and the mixture is mixed/homogenized e.g., by mixing in a shear mixer at a speed of 1000 rpm for about 5 minutes. The mineral component is then added to the mixture and again mixed. The mixing may be again be achieved, e.g., by mixing in a shear mixer, e.g., at 500 rpm for 2 minutes. The mixture in these embodiments may then be frozen at a temperature of −40° C. for 12 hours; and the mixture may be freeze dried e.g., for 48 hours.

Methods of Use

Also provided herein are methods that include inserting any of the present bone grafts into a mammal in need of the bone graft. By way of example, the present bone grafts may be inserted into or administered to a mammal by surgically inserting one or more of the present bone grafts into a mammal, such as a mammal, in need thereof. The bone grafts may be inserted or administered for example by themselves e.g., in the form of a strip, putty, gel and/or sponge, or the bone graft may be available in conjunction with an implant, such as being incorporated therein or thereon (e.g., as a coating). The bone grafts may be inserted in an effective amount, as can be determined by a physician taking into account the need for the bone graft, the type of bone graft, and the patient.

As previously indicated, the subject/patient may be a mammal (as well as other animals), and the mammal may be (but does not have to be) human.

Embodiments of the present invention may include moldable and shapeable putty compositions that may be used for example to fill bone defects. Thus, according to example embodiments the present bone grafts may be for example in the form of a putty or other semi-solid or solid form, including, but not limited to, strip, putty, gel or sponge.

Implants

Yet further example embodiments are directed to implants or other devices or products that include one more of the bone grafts provided herein, incorporated into, or on the implant, or otherwise used with the product or implant. For example, the present bone graft substitutes may be used as a graft within or inside an implant. By way of non-limiting example, bone grafts may be used in conjunction with interbody spacers for treatment of compression fractures.

Surgical implants and compositions should be biocompatible to successfully perform their intended function. Biocompatibility may be defined as the characteristic of an implant or composition acting in such a way as to allow its therapeutic function to be manifested without secondary adverse affects such as toxicity, foreign body reaction or cellular disruption. To help avoid adverse reaction, example bone grafts may be prepared in sterile environments and formulations for implantation into a mammal.

Kits

Yet further embodiments are directed to kits that include one or more of the present bone grafts or one or more components or ingredients thereof.

Example kits may include for example, any of the present bone grafts, along with instructions and/or at least one additional component (such as devices, implants, tools) that may be used for example in the storage, preparation or use of the bone graft substitutes. By way of example, the kit components may be used to assist in adding the bone graft to a device or implant, or to assist in inserting the bone graft into a mammal. Further non-limiting examples may include one or more of the present bone grafts and instructions for the preparation of the bone graft, instructions for the use of the bone graft, a tool for insertion of the bone graft into a mammal, a tool or vehicle for hydration of a dry form of the bone graft, and/or an implant to be inserted into the mammal with the bone graft. For example, the bone graft may be provided in a syringe for reconstitution and/or administration to a mammal/patient. According to example embodiments, products may be provided in a syringe with an attachment to deliver product in a minimally invasive manner. Other possible ingredients in kits may include disposal implements or treatment literature.

Yet further non-limiting examples may include one or more ingredients of the present bone grafts, which may be combined, mixed or treated to prepare the present bone grafts. By way of example, the present kits may include collagen Type 1, one or more minerals, and/or other required or optional ingredients of the present bone grafts, which may be combined, mixed or treated in order to form the present bone grafts. Further provided may be instructions for preparation of one or more of the present bone grafts and/or one or more tools, devices, implants, and/or other components to assist in making or using the present bone grafts.

The following examples are provided to further illustrate various non-limiting embodiments and techniques. It should be understood, however, that these examples are meant to be illustrative and do not limit the scope of the claims. As would be apparent to skilled artisans, many variations and modifications are intended to be encompassed within the spirit and scope of the invention.

EXAMPLES Example 1

According to non-limiting example embodiments, bone grafts are prepared which include collagen type I and one or more different types of mineral, having one or more different rates of dissolution and/or having one or more sizes. The method includes the following:

(1) collagen type I from bovine or porcine source is obtained from either skin (dermal) or tendon.

(2) 20% to 95% Collagen Type 1 (by weight) is mixed with hyaluronic acid (0.2 to 20% by weight) and mixed in a beaker until the desired consistency is reached. Acid (such as HCl) or a base (such as NaOH) can be added to the mixture until a homogenous mixture and desired pH is produced. The pH of the mixture can be for example, between 2.0 and 6.0. (3) Cover mixture and place into refrigerator for 20 to 72 hours.

(4) After refrigerating the mixture (step 3) use a shear mixture to further mix to fully combine into a homogenous mixture

(5) Weigh out mineral(s) (such as calcium phosphate, carbonate apatite, and/or calcium carbonate) and/or demineralized bone matrix

-   -   a) Mineral can include for example, any of the following: in         combination or alone:         -   Beta-tricalcium phosphate (size ranging from 75 nm to 500             μm),         -   carbonate apatite (size ranging from 75 nm to 500 μm), and         -   calcium carbonate (size ranging from 75 nm to 500 μm).         -   b) The total weight percent of minerals in the bone graft             can range from 20% to 95%         -   c) The total weight percent of DBM in the bone graft can             range from 20% to 95%.

(6) Add mineral(s) to the collagen mixture or vice versa. The mixture can be with or without hyaluronic acid.

(7) Mix using a shear mixer.

(8) Place mixture in a refrigerator for 30 minutes to 5 hours.

(9) Remove the mixture from refrigerator.

(10) Neutralize mixture with an acid such as HCl or with a base such as NaOH until the pH is between 6.5 and 8.5.

(11) Pour the mixture into a tray; the tray material can be metal or polymer-based.

(12) The mixture, once in the tray, can be spread using a metal sheet press.

(13) Cover mixture and place into refrigerator for 1 hour to 24 hours.

(14) Blast chill mixture in the freezer at —40° C. (or at least a temperature of less than —20° C.) for 1 hour up to 24 hours.

(15) Freeze dry mixture for 24 to 72 hours to form a “dried pad” mixture.

(16) Take dried pad mixture and cross link; either chemical or physical methods of cross linking may be used.

(17) Rinse the pad if used a chemical cross linking method.

(18) Freeze dry.

(19) Stamp/cut out to desired dimensions.

In the foregoing specification, the invention has been described with reference to specific embodiments thereof. It will, however, be evident that various modifications and changes may be made thereto without departing from the broader spirit and scope of the invention. Accordingly, it is intended that such changes and modifications fall within the scope of the present invention as defined by the claims appended hereto. The specification and drawings are, accordingly, to be regarded in an illustrative rather than restrictive sense. 

We claim:
 1. A bone graft comprising: 20% to 95% by weight of collagen type I with respect to a total weight of the bone graft, and 20% to 95% by weight of one or more minerals with respect to the total weight of the bone graft, wherein the one or more minerals have two or more dissolution rates, thereby allowing the bone graft to enhance bone healing in both early and late phases of bone healing.
 2. The bone graft of claim 1, further comprising 0.2 to 20% by weight of hyaluronic acid with respect to the total weight of the bone graft.
 3. The bone graft of claim 1, further comprising 0.1 to 20% by weight of acid or base with respect to the total weight of the bone graft.
 4. The bone graft of claim 1, further comprising 20% to 95% by weight DBM with respect to the total weight of the bone graft.
 5. The bone graft of claim 1, wherein the collagen type I is from a bovine or porcine source and is obtained from either skin (dermal) or tendon.
 6. The bone graft of claim 1, wherein the one or more minerals comprise beta-tricalcium phosphate.
 7. The bone graft of claim 1, wherein the one or more minerals comprise carbonate apatite.
 8. The bone graft of claim 1, wherein the one or more minerals comprise calcium carbonate.
 9. The bone graft of claim 1, wherein the one or more minerals have a size ranging from about 75 nm to 500 μm.
 10. The bone graft of claim 1, wherein the one or more minerals include a first mineral having a first dissolution profile and a second mineral having a second dissolution profile, wherein the first dissolution profile is different from the second dissolution profile in order to provide two or more different dissolution rates.
 11. The bone graft of claim 1, wherein the bone graft is cross-linked.
 12. A bone graft comprising: 20% to 95% by weight of collagen type I with respect to a total weight of the bone graft, and 20% to 95% by weight of one or more minerals with respect to the total weight of the bone graft, wherein the one or more minerals have different dissolution properties and/or sizes than one another.
 13. The bone graft of claim 12, further comprising 0.2 to 20% by weight of hyaluronic acid with respect to the total weight of the bone graft.
 14. The bone graft of claim 12, further comprising 0.1 to 20% by weight of acid or base with respect to the total weight of the bone graft.
 15. The bone graft of claim 12, further comprising 20% to 95% by weight DBM with respect to the total weight of the bone graft.
 16. The bone graft of claim 12, wherein the collagen type I is from bovine or porcine source and is obtained from either skin (dermal) or tendon.
 17. The bone graft of claim 12, wherein the one or more minerals comprise beta-tricalcium phosphate.
 18. The bone graft of claim 12, wherein the one or more minerals comprise carbonate apatite.
 19. The bone graft of claim 12, wherein the one or more minerals comprise calcium carbonate.
 20. The bone graft of claim 12, wherein the one or more minerals have a size ranging from about 75 nm to 500 μm. 